A general methodology to measure the light-to-heat conversion efficiency of solid materials

Kai Gu; Haizheng Zhong

doi:10.1038/s41377-023-01167-6

Go to Nature Website

Your Location：

Home >

Browse articles >

A general methodology to measure the light-to-heat conversion efficiency of solid materials

Original Articles

- A general methodology to measure the light-to-heat conversion efficiency of solid materials
- A general methodology to measure the light-to-heat conversion efficiency of solid materials
- 光：科学与应用 2023年12卷第6期页码：1051-1060
- Affiliations：
  
  Beijing Key Laboratory of Nanophotonics & Ultrafine Optoelectronic Systems, School of Materials Sciences & Engineering, Beijing Institute of Technology, 100081 Beijing, China
- Author bio：
  
  Haizheng Zhong (hzzhong@bit.edu.cn)
- Funds：
- DOI：10.1038/s41377-023-01167-6
  中图分类号：
- 纸质出版日期：2023-6-30，
  
  网络出版日期：2023-5-17，
  
  收稿日期：2023-1-8，
  
  修回日期：2023-4-9，
  
  录用日期：2023-4-23
Scan for full text
A general methodology to measure the light-to-heat conversion efficiency of solid materials[J]. 光：科学与应用, 2023,12(6):1051-1060.

Gu, K. & Zhong, H. Z. A general methodology to measure the light-to-heat conversion efficiency of solid materials. Light: Science & Applications, 12, 1051-1060 (2023).
A general methodology to measure the light-to-heat conversion efficiency of solid materials[J]. 光：科学与应用, 2023,12(6):1051-1060. DOI： 10.1038/s41377-023-01167-6.

Gu, K. & Zhong, H. Z. A general methodology to measure the light-to-heat conversion efficiency of solid materials. Light: Science & Applications, 12, 1051-1060 (2023). DOI： 10.1038/s41377-023-01167-6.

摘要

Abstract

Light-to-heat conversion has been intensively investigated due to the potential applications including photothermal therapy and solar energy harvesting. As a fundamental property of materials

accurate measurement of light-to-heat conversion efficiency (LHCE) is of vital importance in developing advanced materials for photothermal applications. Herein

we report a photothermal and electrothermal equivalence (PEE) method to measure the LHCE of solid materials by simulating the laser heating process with electric heating process. The temperature evolution of samples during electric heating process was firstly measured

enabling us to derive the heat dissipation coefficient by performing a linear fitting at thermal equilibrium. The LHCE of samples can be calculated under laser heating with the consideration of heat dissipation coefficient. We further discussed the effectiveness of assumptions by combining the theoretical analysis and experimental measurements

supporting the obtained small error within 5% and excellent reproducibility. This method is versatile to measure the LHCE of inorganic nanocrystals

carbon-based materials and organic materials

indicating the applicability of a variety of materials.

关键词

Keywords

references

Yang,X.D.etal.Anultrathinflexible2Dmembranebasedonsingle-wallednanotube–MoS2hybridfilmforhigh-performancesolarsteamgeneration.Adv. Funct. Mater.28,1704505(2018)..

Wu,L.etal.Highlyefficientthree-dimensionalsolarevaporatorforhighsalinitydesalinationbylocalizedcrystallization.Nat. Commun.11,521(2020)..

Hessel,C.M.etal.Copperselenidenanocrystalsforphotothermaltherapy.Nano Lett.11,2560–2566(2011)..

Li,D.etal.Supra-(carbonnanodots)withastrongvisibletonear-infraredabsorptionbandandefficientphotothermalconversion.Light Sci. Appl.5,e16120(2016)..

Wang,K.etal.Melanin–perovskitecompositesforphotothermalconversion.Adv. Energy Mater.9,1901753(2019)..

Meyer,S.M.etal.Sizeeffectsingoldnanorodlight-to-heatconversionunderfemtosecondillumination.J. Phys. Chem. C125,16268–16278(2021)..

Tian,Q.etal.HydrophilicCu9S5nanocrystals:aphotothermalagentwitha25.7%heatconversionefficiencyforphotothermalablationofcancercellsinvivo.ACS Nano5,9761–9771(2011)..

Mazzanti,A.etal.Light–heatconversiondynamicsinhighlydiversifiedwater-dispersedhydrophobicnanocrystalassemblies.Proc. Natl. Acad. Sci. USA116,8161–8166(2019)..

Tian,Q.etal.Hydrophilicflower-likeCuSsuperstructuresasanefficient980nmlaser-drivenphotothermalagentforablationofcancercells.Adv. Mater.23,3542–3547(2011)..

Wang,J.etal.High-performancephotothermalconversionofnarrow-bandgapTi2O3nanoparticles.Adv. Mater.29,1603730(2017)..

Tan,C.L.etal.Preparationofultrathintwo-dimensionalTixTa1-xSyOznanosheetsashighlyefficientphotothermalagents.Angew. Chem. Int. Ed. Engl.56,7842–7846(2017)..

Zhang,S.M.etal.Ultrathintungstenbronzenanowireswithefficientphoto-to-thermalconversionbehavior.Chem. Mater.30,8727–8731(2018)..

Wei,X.etal.Apolyanilinenanofiberarraysupportedultrathinpolyamidemembraneforsolar-drivenvolatileorganiccompoundremoval.J. Mater. Chem. A10,20424–20430(2022)..

Xi,D.M.etal.NIRlight-drivingbarrier-freegrouprotationinnanoparticleswithan88.3%photothermalconversionefficiencyforphotothermaltherapy.Adv. Mater.32,1907855(2020)..

Wang,Y.etal.Cocrystalsstrategytowardsmaterialsfornear-infraredphotothermalconversionandimaging.Angew. Chem. Int. Ed. Engl.57,3963–3967(2018)..

Cao,Y.Y.etal.HighlyefficientNIR-Ⅱphotothermalconversionbasedonanorganicconjugatedpolymer.Chem. Mater.29,718–725(2017)..

Li,X.Z.etal.Biodegradableπ-conjugatedoligomernanoparticleswithhighphotothermalconversionefficiencyforcancertheranostics.ACS Nano13,12901–12911(2019)..

Su,J.etal.Persistentradicaltetrathiafulvalene-based2Dmetal-organicframeworksandtheirapplicationinefficientphotothermalconversion.Angew. Chem. Int. Ed. Engl.60,4789–4795(2021)..

Zhao,L.Y.etal.Supramolecularphotothermaleffects:apromisingmechanismforefficientthermalconversion.Angew. Chem. Int. Ed. Engl.59,3793–3801(2020)..

Arami,H.etal.Remotelycontrollednear-infrared-triggeredphotothermaltreatmentofbraintumoursinfreelybehavingmiceusinggoldnanostars.Nat. Nanotechnol.17,1015–1022(2022)..

Zhu,H.J.etal.Ternarychalcogenidenanosheetswithultrahighphotothermalconversionefficiencyforphotoacoustictheranostics.Small13,1604139(2017)..

Cai,R.etal.PlasmonicAuPt@CuSheterostructurewithenhancedsynergisticefficacyforradiophotothermaltherapy.J. Am. Chem. Soc.143,16113–16127(2021)..

Bao,X.etal.Invivotheranosticswithnear-infrared-emittingcarbondots—highlyefficientphotothermaltherapybasedonpassivetargetingafterintravenousadministration.Light Sci. Appl.7,91(2018)..

Zhu,L.L.etal.Recentprogressinsolar-driveninterfacialwaterevaporation:advanceddesignsandapplications.Nano Energy57,507–518(2019)..

Tao,P.etal.Solar-driveninterfacialevaporation.Nat. Energy3,1031–1041(2018)..

Xu,D.X.etal.Insightsintothephotothermalconversionof2DMXenenanomaterials:synthesis,mechanism,andapplications.Adv. Funct. Mater.30,2000712(2020)..

Zhu,L.L.etal.Solar-drivenphotothermalnanostructuredmaterialsdesignsandprerequisitesforevaporationandcatalysisapplications.Mater. Horiz.5,323–343(2018)..

Zhou,L.etal.Therevivalofthermalutilizationfromthesun:interfacialsolarvaporgeneration.Natl. Sci. Rev.6,562–578(2019)..

Mateo,D.etal.Fundamentalsandapplicationsofphoto-thermalcatalysis.Chem. Soc. Rev.50,2173–2210(2021)..

Li,Y.G.etal.Generalheterostructurestrategyofphotothermalmaterialsforscalablesolar-heatinghydrogenproductionwithouttheconsumptionofartificialenergy.Nat. Commun.13,776(2022)..

Xu,S.Y.,Bai,X.L.&Wang,L.Y.Explorationofphotothermalsensorsbasedonphotothermallyresponsivematerials:abriefreview.Inorg. Chem. Front.5,751–759(2018)..

Zahedian,M.etal.Studiesofnanoparticle-assistedphotoannealingofpolydimethylsiloxanebytime-harmonicphotothermalmicroscopy.ACS Photonics7,2601–2609(2020)..

Zhang,D.L.etal.Bond-selectivetransientphaseimagingviasensingoftheinfraredphotothermaleffect.Light Sci. Appl.8,116(2019)..

Roper,D.K.,Ahn,W.&Hoepfner,M.Microscaleheattransfertransducedbysurfaceplasmonresonantgoldnanoparticles.J. Phys. Chem. C111,3636–3641(2007)..

Richardson,H.H.etal.Experimentalandtheoreticalstudiesoflight-to-heatconversionandcollectiveheatingeffectsinmetalnanoparticlesolutions.Nano Lett.9,1139–1146(2009)..

Alrahili,M.etal.Morphologydependenceinphotothermalheatingofgoldnanomaterialswithnear-infraredlaser.J. Phys. Chem. C124,4755–4763(2020)..

Chen,H.J.etal.Understandingthephotothermalconversionefficiencyofgoldnanocrystals.Small6,2272–2280(2010)..

Regli,S.etal.Photothermalresponseofphotoluminescentsiliconnanocrystals.J. Phys. Chem. Lett.3,1793–1797(2012)..

Wang,X.C.etal.Understandingthephotothermaleffectofgoldnanostarsandnanorodsforbiomedicalapplications.RSC Adv.4,30375–30383(2014)..

Paściak,A.etal.Standardizationofmethodologyoflight-to-heatconversionefficiencydeterminationforcolloidalnanoheaters.ACS Appl. Mater. Interfaces13,44556–44567(2021)..

Almond,D.P.&Patel,P.M.Photothermalscienceandtechniques.(Dordrecht:Springer,1996).

Eriksson,T.S.&Granqvist,C.G.Radiativecoolingcomputedformodelatmospheres.Appl. Opt.21,4381–4388(1982)..

Rong,F.X.etal.ChemicalsynthesisofCu2Senanoparticlesatroomtemperature.Mater. Res. Bull.47,92–95(2012)..

浏览量

Downloads

CSCD

文章被引用时，请邮件提醒。

Submit

工具集

关联资源

暂无数据